Liquid crystalline nature of poly(di-n-hexylsilane)

P. Weber^{1, 2}, D. Guillon^{1, 2}, A. Skoulios^{1, 2} et R.D. Miller<sup>3

1</sup>  Groupe des Matériaux Organiques, Institut Charles Sadron (CRM-EAHP), CNRS-ULP, 6 rue Boussingault, 67083 Strasbourg Cedex, France
²  Institut de Physique et Chimie des Matériaux de Strasbourg, UM 380046, CNRS-ULP-EHICS, Strasbourg, France
³  IBM Almaden Research Center, San Jose, California 95120-6099, USA

Abstract
Polarizing optical microscopy and X-ray diffraction were used to study the structure of poly(di-n-hexylsilane) as a function of temperature. Liquid crystalline in nature, the polymer above 42 °C shows hexagonal columnar symmetry, with the columns formed of single polymer chains. The stacking period of the dihexylsilicon repeat units along the columnar axis is of about 1.56 Å. Far from being all-trans as in the low-temperature crystal, the backbone conformation in the high-temperature mesophase is presumably close to an all-gauche helical conformation.

Résumé
Dans ce travail, on étudie par diffraction des rayons X et microscopie optique en lumière polarisée la structure en fonction de la température d'un poly(di-n-hexylsilane). Au-dessus de 42 °C, la structure correspond à une phase liquide cristalline colomnaire de type hexagonal, chaque colonne étant formée par une chaîne macromoléculaire. La période d'empilement des unités répétitives dihexylsilicium le long de l'axe colomnaire est voisine de 1.56 Å. Loin d'être toute trans comme dans le cristal à basse température, la conformation des chaînes d'atomes de silicium est vraisemblablement proche d'une conformation hélicoïdale toute-gauche.