Increase of Tc in YBa2Cu3O7-δ due to an atomic ordering transition within the orthorhombic phase

M.T. Beal-Monod

Laboratoire de Physique des Solides , Université Paris XI, Bât. 510, 91405 Orsay Cedex, France

Abstract
We recently showed that a long-range atomic ordering transition may be expected in YBa2Cu3O7- δ (0 ≤ δ ≤ 0.5 ) at a temperature T'0 much below the orthorhombic-tetragonal one To. Assuming that the disordering linked to the occurrence of T'0 acts as a pair breaking parameter, we examine the resulting variation ΔTc of the superconducting temperature for varying δ. Compared to the so far measured Tc corresponding to a state of order quenched from T > T'0, the increase of Tc, when T < T'0, ΔTc is expected to be maximum around δ ˜ 0.4.

Résumé
Nous avons récemment montré qu'on peut attendre une transition d'ordre atomique à longue distance dans YBa2Cu3O7- δ à une température T'0 bien en dessous de la transition tétragonal-orthorhombic T0. En supposant que le désordre lié à l'existence de T'0 agit comme paramètre de pair-breaking, nous examinons la variation ΔTc qui en résulte pour la température de supraconductivité à δ variable. En comparaison avec les Tc mesurés jusqu'à présent et correspondant à un état d'ordre trempé depuis T > T'0, l'accroissement prévu pour Tc, ΔTc, quand T < T'0, devrait être maximum autour de δ ˜ 0,4.

PACS
6470K - Solid-solid transitions.
7410 - Occurrence, potential candidates.
7470 - Superconducting materials.

Key words
barium compounds -- order disorder transformations -- superconducting transition temperature -- type II superconductors -- yttrium compounds