The structure of decagonal Al7(Mn1-xFe x)2 alloys

P.J. Schurer1, T.J. van Netten2 et L. Niesen2

1  Laboratorium voor Vaste Stof Fysica, Materials Science Centre, University of Groningen, Groningen, The Netherlands
2  Laboratorium voor Algemene Natuurkunde, Materials Science Centre, University of Groningen, Groningen, The Netherlands


Abstract
Radial distribution functions around the Mn atom have been derived from EXAFS measurements on decagonal Al7(Mn1-xFe x)2, x = 0 and x = 0.3. Analysis indicates that the same structural units exist in decagonal as in icosahedral Al-Mn alloys and α-AlMnSi. These structural units with local icosahedral symmetry form a framework with long range decagonal symmetry.


Résumé
Les fonctions de distribution radiales autour de l'atome Mn ont été déduites de mesures EXAFS dans Al7(Mn1-xFe x)2 décagonal, avec x = 0 et x = 0,3. Cette analyse montre que les mêmes unités structurales existent dans la phase icosahédrique et la phase décagonale des alliages Al-Mn et α-AlMnSi. Ces unités structurales avec symétrie locale icosahédrique forment un réseau avec une symétrie décagonale à longue portée.

PACS
6143 - Disordered solids.
6166D - Alloys.

Key words
aluminium alloys -- crystal symmetry -- EXAFS -- iron alloys -- manganese alloys -- quasicrystals