J. Phys. France 47, 1221-1226 (1986)
DOI: 10.1051/jphys:019860047070122100

The magnetic susceptibility of graphite biintercalated with CoCl2 and GaCl3

I. Rosenman¹, F. Batallan¹, Ch. Simon¹ et L. Hachim<sup>2

1</sup>  Groupe de Physique des Solides de l'Ecole Normale Supérieure , Université de Paris V, Tour 23, 2, place Jussieu, 75251 Paris Cedex 05, France
²  Laboratoire de Chimie Minérale Appliquée (A. Herold) , Université de Nancy I, B.P. 239, 54506 Vandoeuvre lès Nancy Cedex. France

Abstract
We present the first results of magnetic susceptibility on CoCl2-GaCl 3 biintercalated in graphite, and compare them with those obtained in second stage CoCl2-graphite. A fit by a power law above the maximum of the susceptibility present two regimes : in the high temperature one, the γ values are high and even higher in the CoCl2-GaCl 3 compound. This indicates that the three-dimensional coupling is lower in the biintercalation compound. In the low temperature regime, near the transition, the susceptibility is driven by the islandic nature of the intercalate layer.

Résumé
Nous présentons les premiers résultats obtenus par susceptibilité magnétique sur le composé de bi-insertion du graphite avec CoCl2-GaCl3 et nous les comparons à ceux du composé d'insertion graphite-CoCl2 de deuxième stade. L'ajustement de la partie haute température du pic de susceptibilité présente deux régimes. Dans le régime haute température, les valeurs de γ obtenues sont élevées, et plus élevées encore dans le biinséré. Ceci indique que le couplage tridimensionnel est encore plus faible dans ce dernier. Dans le régime basse température, près de la transition, la susceptibilité est gouvernée par la nature insulaire des couches insérées.

PACS
7530C - Saturation moments and magnetic susceptibilities.

Key words
cobalt compounds -- gallium compounds -- graphite -- intercalation compounds -- magnetic susceptibility