J. Phys. France 46, 979-986 (1985)
DOI: 10.1051/jphys:01985004606097900

Anomalous spectral density and two-level system-phonon coupling in an insulating magnetic glass

P. Doussineau¹, A. Levelut¹, M. Matecki², W. Schön¹ et W.D. Wallace<sup>1

1</sup>  Laboratoire d'Ultrasons, Université Pierre et Marie Curie, Tour 13, 4, place Jussieu, 75230 Paris Cedex 05, France
²  Laboratoire de Chimie Minérale D, Université de Rennes Beaulieu. 35042 Rennes Cedex, France

Abstract
Low temperature ultrasonic measurements on the magnetic glass (MnF 2)0.65(BaF2)0.2(NaPO3) 0.15 in the 0.1-1 GHz range give a value for the spectral density P of two level systems (TLS) two orders of magnitude smaller than usual and very large values for the TLS-phonon coupling constants γ1 and γt. Comparison with the case of the non-magnetic glass (ZnF2)0.6(BaF2)0.2(NaPO3 )0.2 suggests that these anomalous values are related to the magnetic properties of the glass.

Résumé
Des mesures ultrasonores aux basses températures, dans la gamme de fréquence 0,1-1 GHz ont été faites sur le verre magnétique (MnF2)0,65 (BaF2)0,2(NaPO3)0,15. La densité spectrale, P des systèmes à 2 niveaux (S2N) est deux ordres de grandeur plus petite que dans les autres verres tandis que les constantes de couplage S2N-phonon γ1 et γt sont anormalement grandes. La comparaison avec les mesures effectuées sur le verre non magnétique (ZnF2)0,6(BaF2)0,2(NaPO3 )0,2 suggère un lien entre ces valeurs anormales et les propriétés magnétiques du verre.

PACS
6265 - Acoustical properties of solids.
7540 - Critical-point effects, specific heats, short-range order.
7550K - Amorphous and quasicrystalline magnetic materials.

Key words
barium compounds -- magnetic properties of amorphous substances -- manganese compounds -- phosphate glasses -- sodium compounds -- spin glasses -- ultrasonic absorption -- ultrasonic velocity