Intrinsic viscosity of flexible macromolecules : transition from theta to collapsed state

R. Perzynski1, 2, M. Delsanti1 et M. Adam1

1  Service de Physique du Solide et de Résonance Magnétique, CEN-Saclay, 91191 Gif-sur-Yvette Cedex, France
2  Present address: Laboratoire d'Ultrasons, université P. et M. Curie, Tour 13, 4 place Jussieu, 75230 Paris Cedex 05, France


Abstract
Intrinsic viscosity measurements have been performed on polystyrene-cyclohexane system as a function of temperature T (T ≲ θ and as a function of molecular weight (8.2 x 10 4 ≤ Mw ≤ 2.06 x 107) .The expansion factor α3 η = [η]/[ηθ] of the intrinsic viscosity [η] scales with the reduced variable (T - θ/T) · ∫M w. For (T-θ/T) º √Mw ≲ - 40, the intrinsic viscosity of a collapsed macromolecule is found to be independent of molecular weight A value ν = 1/3 is therefore given to the index relating size to molecular weight.


Résumé
Des mesures de viscosité intrinsèque [η] sont effectuées sur des solutions diluées de polystyrène dans le cyclohexane en fonction de la température (T ≲ 0) et de la masse moléculaire (8,2 x 104 ≤ M w ≤ 2,06 x 107). Le facteur d'expansion (α 3η = [η]/[ ηθ]) de la viscosité intrinsèque obéit à une loi d'échelle dont la variable réduite est (T - θ/T) · √Mw Lorsque (T - θ/T) · √Mw ≲ - 40, la viscosité intrinsèque d'une chaîne effondrée est indépendante de la masse moléculaire. L'indice ν reliant la taille à la masse moléculaire est trouvé égal à 1/3.