On the stabilization of A-15 Nb3Ge with high TC's

F. Weiss, O. Demolliens, R. Madar, J.P. Senateur et R. Fruchart

ER. 155, ENSIEG, Domaine Universitaire, B.P. 46, 38402 St Martin d'Hères, France


Abstract
High-Tc A-15 Nb3Ge superconductors have been prepared by chemical vapour deposition. Superconducting transition temperatures, crystal structures, and growth morphology for different samples are reported here. From the analytical results we hypothesize that stoichiometric high-Tc Nb3Ge can be formed through a heteroepitaxial process between the A-15 and the competing Nb5Ge3 phases which have close structural relations.


Résumé
Le composé supraconducteur Nb3Ge de structure A-15 et de température critique Tc ≳ 20 K a été préparé par dépôt chimique en phase vapeur (CVD). Les résultats de mesure des températures de transition supraconductrice, l'analyse de la morphologie des dépôts et l'analyse structurale des différentes phases obtenues nous conduisent à proposer une hypothèse selon laquelle le composé Nb3Ge stoechiométrique de température critique élevée est stabilisé par le biais de relations d'hétéroépitaxie entre la phase. A-15 et l'une des phases de formule Nb5Ge 3 (type W5Si3 ou Mn5Si3) qui présentent des relations structurales très étroites avec la phase A-15.

PACS
7478D - Low-Tc films.

Key words
crystal atomic structure of inorganic compounds -- crystal morphology -- germanium alloys -- niobium alloys -- superconducting thin films -- superconducting transition temperature -- type II superconductors -- vapour phase epitaxial growth