On the magnetic properties of B2O3-Pbo-Fe2O 3-K2O and B2O3-PbO-Fe 2O3-CaO glasses

E. Burzo1, D. Ungur1 et I. Ardelean2

1  National Center of Physics, PO Box 5206, Bucharest, Romania
2  Faculty of Physics, University of Cluj-Napoca, Romania


Abstract
The 20 Fe2O380[3 B2O3(1 - x)PbOxAuOv,] glasses with A uOv = K2O and CaO were studied by magnetic and Mössbauer effect measurements. The variation of the fraction r of ferrous ions is proportional to the difference between the valence of A ions and that of lead as well as to AuOv content. The composition dependence of r values is analysed in correlation with the glass composition.


Résumé
Nous présentons les résultats de mesures magnétiques et par effet Mössbauer effectuées sur des verres 20 Fe2O380[3 B2O 3(1 - x)PbOxAuOv] avec A uOv = K2O ou CaO. La modification de la fraction r des ions Fe2+ est proportionnelle à la différence entre la valence des ions A et celle du plomb ainsi qu'au contenu en A uOv. La variation avec la composition des valeurs de r est analysée en corrélation avec la composition des verres.

PACS
7680 - Mössbauer effect; other gamma-ray spectroscopy.
7550K - Amorphous and quasicrystalline magnetic materials.

Key words
borate glasses -- boron compounds -- calcium compounds -- iron compounds -- lead compounds -- Mossbauer effect -- potassium compounds