J. Phys. France 41, 1141-1145 (1980)
DOI: 10.1051/jphys:0198000410100114100

Temperature dependence of the samarium oxidation state in SmB6 and Sm1-xLaxB6

J.M. Tarascon¹, Y. Isikawa¹, B. Chevalier¹, J. Etourneau¹, P. Hagenmuller¹ et M. Kasaya<sup>2

1</sup>  Laboratoire de Chimie du Solide du C.N. R.S., Université de Bordeaux I, 351, cours de la Libération, 33405 Talence, Cedex, France
²  Department of Physics, Faculty of Science, Tohoku University, Sendai, Japan

Abstract
The cubic lattice parameter temperature dependence of SmB6 between 300 K and 4.2 K as well as the X-ray absorption at the LIII edge measured in the same temperature range, give direct evidence of the average samarium valence change which goes from 2.60 at 300 K to 2.53 at 4.2 K. Previous work claimed that the Sm2+ : Sm3+ ratio was temperature independent in SmB6. As for SmB6 a samarium valence change has been observed with decreasing temperature below 300 K in the Sm 0.75La0.25B6 solid solution.

Résumé
La variation thermique du paramètre de la maille cristalline de SmB 6 ainsi que des mesures d'absorption X (seuil LIII du samarium) effectuées entre 4,2 K et 300 K mettent en évidence une variation du degré d'oxydation moyen du samarium qui passe de 2,60 à 300 K à 2,53 à 4,2 K. Les travaux antérieurs jusqu'à présent indiquaient que le rapport Sm2+/Sm 3+ était indépendant de la température. Un comportement analogue à celui de SmB6 a été observé pour la solution solide Sm 0,75La 0,25B6.

PACS
8165C - Surface cleaning, etching, patterning.
7870D - X-ray absorption spectra.
8165C - Surface cleaning, etching, patterning.

Key words
lanthanum compounds -- lattice constants -- oxidation -- samarium compounds -- X ray absorption spectra