Valence transition of samarium in hexaboride solid solutions Sm 1-xMxB6 (M = Yb 2+ , Sr2+ , La3+ , Y3+ , Th4+ )
J.M. Tarascon1, Y. Isikawa1, 2, B. Chevalier1, J. Etoumeau1, P. Hagenmuller1 et M. Kasaya21 Laboratoire de Chimie du Solide du C.N.R.S., Université de Bordeaux I, 351, cours de la Libération, 33405 Talence Cedex, France
2 Department of Physics, Faculty of Science, Tohoku University, Sendai, Japan.
Abstract
The X-ray absorption measurements at the LIII edge have been carried out at 300 K in the solid solutions Sm1-xMxB 6 (M = Yb2+, Sr2+, La3+, Y3+, Th4+). The fine structure of the edge indicates that the average samarium valence tends towards Sm3+ with increasing Yb2+ and Sr2+ contents whereas the substitutions with La 3+, Y3+ and Th4+ involve a decrease of the average samarium valence reaching Sm2+ as x increases. The entire results obtained agree well with those deduced from the analysis of the cubic lattice parameter variation and from the magnetic susceptibility measurements.
Résumé
Des mesures d'absorption X (seuil LIII du samarium) ont été effectuées à 300 K sur les solutions solides Sm1- xMxB6 (M = Yb2+, Sr 2+, La3+, Y3+, Th4+). Lorsque x croit la variation des intensités des pics correspondant au seuil LIII des configurations Sm2+ : 4f6 et Sm3+ : 4f 5 indique que le degré d'oxydation moyen du samarium tend vers 3 avec Yb2+ et Sr2+ alors qu'il tend vers 2 avec La3+ , Y3+ et Th4+. Les résultats obtenus sont confirmés par les mesures de susceptibilité magnétique et de paramètre cristallin.
7870D - X-ray absorption spectra.
Key words
lanthanum compounds -- lattice constants -- magnetic susceptibility -- samarium compounds -- solid solutions -- strontium compounds -- thorium compounds -- X ray absorption spectra -- ytterbium compounds -- yttrium compounds