J. Phys. France 41, 515-518 (1980)
DOI: 10.1051/jphys:01980004106051500

Irradiations, à basses températures, de Nb3 Ge aux neutrons et aux électrons

F. Rullier¹, S. Païdassi² et Y. Quéré<sup>1

1</sup>  Section d'Etudes des Solides Irradiés, C.E.N., B.P. 6, 92260 Fontenay-aux-Roses, France
²  Département de Métallurgie de Grenoble, C.E.N., Chemin des martyrs, 38 Grenoble, France

Abstract
Superconductive samples of Nb3Ge, of critical temperature Tc ≈ 20 K, were irradiated at ≈ 22 K with fast neutrons and with 2.5 MeV electrons. Temperature Tc decreases under irradiation, the relation between A Tc and Δρ (Δp : increase of residual resistivity) being the same in both cases. This result indicates that the alteration of Tc seems to be due to the homogeneous creation of point defects rather than to the heterogeneous accumulation of displacement cascades.

Résumé
Des échantillons supraconducteurs de Nb3Ge, de température critique Tc ≈ 20 K, ont été irradiés à ≈ 22 K par des neutrons rapides et par des électrons de 2,5 MeV. La température Tc diminue sous irradiation, la loi de variation ΔTc = f(Δp) (Δp : augmentation de résistivité résiduelle) étant la même dans les deux cas. On en déduit que l'effet principal sur Tc est plus celui des défauts ponctuels que celui du désordre créé dans les cascades de déplacements.

PACS
6172J - Point defects (vacancies, interstitials, color centers, etc.) and defect clusters.
6180F - Electron and positron radiation effects.
6180H - Neutron radiation effects.

Key words
electron beam effects -- germanium alloys -- neutron effects -- niobium alloys -- point defects -- superconducting transition temperature -- type II superconductors