Polymorphism of poly(vinylidene fluoride) induced by poling and annealing

B. Servet1, 2 et J. Rault2

1  L.C.R. Thomson C.S.F. Corbeville, 91401 Orsay, France
2  Laboratoire de Physique des Solides, Université Paris-Sud, 91405 Orsay, France


Abstract
In stretched poly(vinylidene fluoride) films, the transition from unpolar α-form to a polar form (αp) is produced by pohng at 80 °C by an electric field of 1 MV/cm. This oriented form has the same lattice constants as α-form but is associated with extra diffuse reflections. This form and the diffuse reflections disappear by annealing above 170 °C and give an oriented and more stable form (α') in which the chain has the T3GT3G- conformation.


Résumé
Dans les films étirés de fluorure de polyvinylidène, l'application d'un champ électrique de 1 MV/cm produit une transformation structurale α non polaire → αp polaire. La phase αp orientée, avec les mêmes paramètres cristallins que la phase α, est toujours accompagnée de taches de Bragg diffuses. Cette structure disparaît par recuit à 170 °C pour donner une nouvelle phase orientée (α') plus stable dans laquelle la chaîne a une conformation T3GT3G -.

PACS
6110 - X-ray diffraction and scattering.
6141 - Polymers, elastomers, and plastics.
8140E - Cold working, work hardening; annealing, post-deformation annealing, quenching, tempering recovery, and crystallization.

Key words
annealing -- polymer films -- polymorphism -- X ray diffraction examination of materials