Atomic displacements in low temperature irradiated chromium crystals

Abstract
Monocrystalline specimens of chromium, cut parallel to the (100), (110) and (111) planes, have been irradiated with electrons in the energy range 0.48-1.7 MeV. The threshold energy for atomic displacement is found to be about equal in the two crystallographic directions < 100 > and < 111 >, although the mechanisms for displacement may be quite different in the two cases. The recovery of the defects has been studied up to 60 K, and after irradiations at 0.5,0.525 and 0.75 MeV. The anisotropy of the different substages appears to bear some resemblance to the low temperature recovery of tungsten. A tentative attribution is given for the various substages up to 40 K.

Résumé
Nous avons irradié des échantillons monocristallins de chrome parallèles aux plans (100), (110) et (111), avec des électrons d'énergie comprise entre 0,48 et 1,7 MeV. Nous avons trouvé que l'énergie seuil de déplacement atomique est sensiblement la meme dans les deux directions cristallographiques < 100 > et < 111 > bien que les mécanismes de déplacement soient vraisemblablement différents. Nous avons étudié le recuit des défauts créés, après irradiation à 0,525 MeV (jusqu'à 60 K), 0,5 et 0,75 MeV. L'anisotropie des premières sous-étapes de recuit présente plusieurs points communs avec le recuit du tungstène dans le même domaine de température. Nous suggérons une interprétation des différentes sous-étapes jusqu'à 40 K.