J. Phys. France 38, 971-976 (1977)
DOI: 10.1051/jphys:01977003808097100

Inelastic light scattering by gel modes in semi-dilute polymer solutions and permanent networks at equilibrium swollen state

J.P. Munch¹, S. Candau¹, J. Herz² et G. Hild<sup>2

1</sup>  Laboratoire d'Acoustique Moléculaire Université Louis-Pasteur, 4, rue Blaise-Pascal, 67070 Strasbourg, France
²  Centre de Recherches sur les Macromolécules, C.N.R.S., 67083 Strasbourg, France

Abstract
The cooperative diffusion constant, determined from light scattering experiments on polymeric networks swollen in a good solvent, varies with equilibrium concentration according to a scaling law similar to that observed in semi-dilute solutions. This result implies that the average distance between adjacent crosslinks of the network is equal to the screening length. This assumption, supported also by compressional modulus data, allows us to reconsider the real structure of polymeric networks and in particular to consider the influence of entanglements trapped during the gelation process.

Résumé
Le coefficient de diffusion coopératif, mesuré par diffusion de la lumière dans des réseaux polymériques gonflés en bon solvant, varie avec la concentration à l'équilibre des gels selon une loi d'échelle identique à celle des solutions semi-diluées. Ce résultat implique que la distance moyenne entre noeuds adjacents du réseau est égale à la longueur d'écran. Cette hypothèse confirmée par les mesures de compression uniaxiale, permet de reconsidérer la structure réelle des réseaux polymériques et en particulier de mettre en évidence l'influence des enchevêtrements piégés durant le processus de réticulation.

PACS
6125H - Macromolecular and polymer solutions; polymer melts; swelling.
7835 - Brillouin and Rayleigh scattering; other light scattering.
8270G - Gels and sols.

Key words
diffusion in liquids -- gels -- light scattering -- polymer solutions