Conductibilité thermique de graphite quasi monocristallin et effets d'irradiation aux neutrons. - I. mesures

Abstract
Measurements of the thermal conductivity K of a pyrolytic graphite annealed under pressure at high température have been made between 6 and 300 °K. Both K// and K parallel and perpendicular to the c axis have been measured successively. The results together with other physical properties show that this graphite is well ordered and very close to a single crystal. k⊥ shows a maximum at about 110 °K and Kll a maximum at about 70 °K. It is possible to state that the measurements of KII are very little affected by the contribution of K. In a first step, the effect of neutron irradiatiod has been studied only K ⊥which is very sensitive to irradiation. With this near-ideal graphite a theoretical analysis of the heat-transport phenomena in graphite is possible and an approach to it is given by B. Dreyfus and R. Maynard in the following paper.

Résumé
On a mesuré entre 6 et 300 °K la conductibilité thermique K d'un graphite pyrolytique recuit sous pression à haute température. K// et K, parallèlement et perpendiculairement à l'axe c, ont été mesurées successivement. Les résultats obtenus ainsi que d'autres mesures physiques montrent que ce graphite est très bien organisé et très voisin du monocristal. Les résultats obtenus pour K⊥ montrent un maximum vers 110 °K et ceux obtenus pour K // montrent un maximum vers 70 °K. Il est possible d'affirmer que la contribution de K⊥ à K// est faible et que l'on a réellement mesuré KII. Dans un premier temps, on a étudié les effets d'irradiations neutroniques seulement sur K qui se montre très sensible au rayonnement. Avec ce graphite quasi monocristallin, une analyse théorique des phénomènes de transport de la chaleur dans le graphite est possible. Cette analyse est abordée par B. Dreyfus et R. Maynard dans l'article suivant.