La magnétostriction du nickel

Abstract
We measured by a dilatometer method the magnetostriction of a nickel sample, purified by the melting zone technique (99.99 % Ni) and carefully annealed ; the effect of small external stresses on the domain structure has been investigated, and the results are compared with those obtained with less pure samples. Our results, obtained with a nickel single crystal, show that Becker's formula λs = 2/5 λ100 + 3/5 λ 111 is only approximate ; on the other hand, they agree fairly well with two formulae, respectively due to Gallissot and Vergne, and Callen and Goldberg : λs = c (2/5 λ100 + 3/5 λ 111) and λs = αλ100 + (1 - α) λ 111, c and α being functions of the elastic anisotropy of nickel. Lastly, it is shown that the isotropic magnetostriction approximation does not permit to treat rigorously the problem of the effect of strong stresses on the magnetostriction of nickel.

Résumé
La magnétostriction d'un échantillon de nickel purifié par fusion de zone (99,99 % Ni) et soigneusement recuit a été mesurée par une méthode dilatométrique ; l'influence de faibles contraintes extérieures sur la structure en domaines a été mise en évidence, et les résultats sont comparés à ceux qu'on obtient sur des échantillons moins purs. Des mesures effectuées sur un monocristal ont montré que la formule de Becker, λ s = 2/5 λ100 + 3/5 λ111, n'est qu'approchée ; en revanche, nos résultats s'accordent bien avec deux formules respectivement proposées par Gallissot et Vergne, et par Callen et Goldberg : λs = c (2/5 λ 100 + 3/5 λ111) et λs = αλ 100 + (1 - α) λ111, où c et α sont deux fonctions de l'anisotropie élastique du nickel. Enfin il est montré que l'approximation de la magnétostriction isotrope ne permet pas de traiter correctement le problème de l'influence des fortes contraintes sur la magnétostriction du nickel.