Étude de la thermoluminescence et de la conductibilité d'un ZnS: Cu, Cl a deux bandes d'émission
T. Ceva et B. LambertLaboratoire de Luminescence, Faculté des Sciences de Paris
Abstract
An electroluminescent ZnS shows two emission bands under UV irradiation (3 650 Å), one blue and the other green. Large spectrum modifications are observed around the thermoluminescence maximum. The glow curves show two types of shallow traps one 0 . 21 eV deep related to the blue emission and the other 0,26 eV deep related to the green emission. Conductivity is observed closely related with the green peak only. These facts suggest that the trap at 0.21 eV interacts with the blue centre.
Résumé
Un sulfure de zinc électroluminescent présente, sous irradiation UV (3 650 Å) deux bandes d'émission : l'une bleue, l'autre verte. On observe de grandes modifications spectrales de l'émission lumineuse aux environs des maximums de thermoluminescence. Celle-ci a montré l'existence de deux pièges l'un à 0,21 eV lié à l'émission bleue, l'autre à 0.26 eV lié à l'émission verte. Seul le pic vert est accompagné de conductibilité. Ces expériences suggèrent une interaction entre le piège à 0,21 eV et le centre bleu.
7860F - Electroluminescence.
Key words
transport processes -- electroluminescence -- luminescence -- semiconductors -- band structure -- thermoluminescence -- zinc compounds