Étude par diffraction de rayons X et par conductibilité électrique de la mise en solution de MgF2 dans Lif
Mireille Benveniste, Estrella Laredo, Pierre Berge et Max TournarieService de Physique du Solide et de Résonance Magnétique, Centre d'Études Nucléaires de Saclay
Abstract
We report X-ray diffraction experiments at high température on powdered LiF single crystals doped with Mg and on mixtures of powdered LiF and MgF 2. We thus verify that the dissolution of precipitated MgF2 accounts for the steep increase of the number of carriers, as observed by electrical conductivity. The dissolution enthalpy appears to be 1.2 eV from both methods. Experiments carried out on mixtures of powdered LiF and MgF 2 confirm this value and demonstrate the high temperature solubility of MgF2 in LiF.
Résumé
Nous avons étudié, par diffraction de rayons X à haute température, des poudres provenant de monocristaux de LiF dopés au magnésium, ou des mélanges de poudres de LiF et de MgF2. Nous avons ainsi vérifié que l'augmentation brusque du nombre de porteurs observée en conductibilité électrique est due à la mise en solution des précipités de MgF2. L'enthalpie nécessaire à cette mise en solution est de 1,2 eV d'après les deux méthodes de mesure. Les expériences portant sur les mélanges de poudres des deux espèces cristallines ont confirmé cette valeur et ont prouvé la grande solubilité de MgF2 dans LiF à haute température.