Recuits de la résistivité électrique produite dans le cuivre par trempe et par irradiation - II. Étude du cuivre irradié aux électrons. Comparaison avec du cuivre trempé

CL. Budin, P. Lucasson et A. Lucasson

Laboratoire de Chimie Physique, Faculté des Sciences de Paris, Centre d'Orsay, Orsay, Seine-et-Oise


Abstract
Using the same specimen, we have carried out alternately irradiation with 1.5 MeV electrons at -175 °C and quencheing in a hydrogen atmosphere. After each quench or eachirradiation, isothermal or isochronal anneals were performed in order to compare the mobilities of the point defects produced in each case. Activation energy determinations are not conclusive. Isochronal anneals show that after irradiation the specimen anneals in stage III at lower temperature than after a quench.


Résumé
Nous avons effectué alternativement sur un même échantillon de cuivre, des irradiations par des électrons de 1,5 MeV à-175 °C et des trempes en atmosphère d'hydrogène. Après chaque irradiation ou trempe, des recuits étaient faits en vue de comparer les mobilités des défauts ponctuels qui recuisent au voisinage de la température ordinaire. Les déterminations d'énergie d'activation ne permettent pas de conclure à une différence. Les recuits isochrones montrent qu'il existe toujours un décalage qui peut atteindre 30 °C entre les températures moyennes des recuits dans le cuivre irradié (étape III) et trempé, le métal irradié recuisant à plus basse température.