Défauts créés par bombardement ionique de couches minces d'or

B. Jouffrey

Laboratoire de Physique des Solides, Faculté des Sciences, Orsay (S.-et-O.)


Abstract
The effects of ion bombardment on thin evaporated crystals of gold have been investigated by means of the electron microscope. Thèse effects are a function of the temperature of the sample. At room temperature the main effect is the production of a great number of dislocation loops. Elongated loops are observed. The behaviour of these defects during annealing shows that these elongated loops are dipoles which appear to be perfect. At 200°C the ion bombarment produces new defects which appear to be argon bubbles. It is possible to observe the condensation of bubbles on to the dislocation loops.


Résumé
Des monocristaux d'or préparés par évaporation ont été soumis à des bombardements ioniques, puis observés au microscope électronique. Les effets dus à ces bombardements dépendent de la température de l'échantillon. A la température ambiante, on observe un grand nombre de boucles de dislocations, parmi lesquelles on observe des boucles de dislocations allongées. Le comportement de ces derniers défauts durant un recuit montre que ce sont des dipôles de dislocations qui semblent être parfaits. A 200 °C le bombardement ionique entraîne la formation de bulles de gaz. Il est possible d'obtenir une condensation de telles bulles sur des boucles de dislocations.

PACS
6172L - Linear defects: dislocations, disclinations.
6180J - Ion radiation effects.

Key words
dislocations -- films -- gold -- heat treatment -- ion beam effects