Dislocations partielles dans un carbure de tantale sous-stoechiométrique

J.L. Martin1 et B. Jouffrey2

1  Office National d'Études et de Recherches Aérospatiales, 92-Châtillon
2  Laboratoire de Physique des Solides, Faculté des Sciences d'Orsay, France


Abstract
It has been shown, in a previous paper, that intrinsic stacking faults are present in a non-stoichiometric carbide (TaC0,75). In the present paper, a study of the detailed orientation of partial dislocations reveals that stacking faults are bounded by Shockley dislocations. The authors conclude that the observed faults are due to a shear. The presence of widely dissociated nodes suggests that the stacking fault energy is low in this composition range.


Résumé
Un article précédent a révélé l'existence de défauts d'empilement intrinsèques dans un carbure sous-stoechiométrique (TaC0,75). Dans la présente étude, l'orientation détaillée de dislocations partielles dans le même carbure a montré que les défauts d'empilement étaient limités par des dislocations de Shockley. Les auteurs concluent que les défauts observés proviennent d'un cisaillement. La présence de noeuds très dissociés permet de penser que l'énergie de faute est faible dans ce domaine de composition.