I.Contribution à l'étude de la propagation des fautes d'empilement dans les métaux cubiques à faces centrées
G. FontainePhysique des Solides, 91 Orsay
Abstract
This paper studies from a theoretical point of view the interaction of a Shockley dislocation cutting through the Frank network of a work-hardened face centered cubic metal. For an isolated stacking fault, a frictional force is deduced mainly due to cutting through the attractive trees, proportional to the square root of the density of the network and sufficient to stabilize the fault, once it is formed. The dipoles created when trees are cut through should prevent the formation of point defects by straining ; they should collect little by little into larger dipoles and finally allow the fault to multiply when it has reached a critical size.
Résumé
On étudie d'un point de vue théorique les interactions d'une dislocation de Shockley qui se propage à travers le réseau de Frank d'un métal cubique à faces centrées écroui. On en déduit, pour une faute d'empilement isolée, une force de frottement essentiellement due à la traversée des arbres attractifs, proportionnelle à la racine carrée de la densité du réseau et suffisante pour stabiliser la faute, une fois celle-ci formée. On montre que les dipôles créés à la traversée des arbres doivent empêcher la formation de défauts ponctuels lors de la déformation ; ils doivent se réunir peu à peu en plus grands dipôles et permettre finalement la multiplication du défaut d'empilement quand celui-ci a pris une extension suffisante.
6172 - Defects and impurities in crystals; microstructure.
Key words
crystal defects -- metals