J. Phys. France 50, 2193-2200 (1989)
DOI: 10.1051/jphys:0198900500160219300

Calculation of phase diagrams for the order-disorder transition in the binary systems Ni-Fe and Ni-Al

P. Cenedese, A. Marty et Y. Calvayrac

Centre d'Etudes de Chimie Métallurgique, C.N.R.S. LP 2801, 15 rue Georges Urbain, 94407 Vitry sur Seine Cedex, France

Abstract
The Cluster Variation Method, in the Tetrahedron-Octahedron approximation, is used to investigate the Ni3Al and Ni3Fe ordering phase diagrams. The pairwise interaction potentials used are extracted from X-ray or neutron diffuse scattering measurements. The calculated phase diagrams are compared to the experimental data. It is shown that, for the case of Ni3Fe, a satisfactory agreement can be achieved by introducing a slight variation of the second-neighbor pair interaction potential as a function of concentration.

Résumé
La Méthode de Variation des Amas, dans l'approximation du Tétraèdre-Octaèdre, est utilisée pour étudier le diagramme d'équilibre des phases au voisinage de la transition ordredésordre, pour Ni3Al et Ni3Fe. Les potentiels d'interaction de paires sont déterminés à partir de mesures de diffusion diffuse des rayons X ou des neutrons. Les diagrammes de phase calculés sont comparés aux données expérimentales. On montre que, dans le cas de Ni3Fe, un accord satisfaisant peut être obtenu en introduisant une faible variation du potentiel d'interaction de paires de seconds voisins en fonction de la concentration.

PACS
6470K - Solid-solid transitions.
8130H - Constant-composition solid-solid phase transformations: polymorphic, massive, and order-disorder.

Key words
aluminium alloys -- iron alloys -- nickel alloys -- order disorder transformations -- phase diagrams -- potential energy functions