Dielectric properties of undoped polyacetylene films in a large frequency range

M. Gamoudi¹, J.J. André², B. François² et M. Maitrot<sup>1

1</sup>  Laboratoire d'Electronique 2, Université Claude-Bernard, Lyon-I, 69622 Villeurbanne, France
²  Centre de Recherches sur les Macromolécules (C.N.R.S.), 67083 Strasbourg Cedex, France

Abstract
Dielectric measurements were performed in a large frequency range (10 -4-10+5 Hz) on undoped cis-polyacetylene samples from several laboratories both with ohmic and blocking contacts. The carrier density is low (2 × 1016 cm-3) and constant but the mobility is thermally activated with a sample and contact dependent activation energy. A maximum activation energy of about 1.6 eV has been found with blocking contacts on the less conducting samples (5 x 10-12 Ω-1 cm-1).

Résumé
Des mesures diélectriques ont été faites dans un intervalle étendu de fréquences ( 10-4-10+5 Hz) sur des échantillons non dopés de cis-polyacétylène provenant de différents laboratoires, en utilisant à la fois des contacts ohmiques et bloquants. La densité de porteurs est faible (2 x 1016 cm-3) et constante; par contre la mobilité est thermiquement activée, avec une énergie d'activation qui dépend des échantillons et des contacts. Dans le cas de contacts bloquants et sur les échantillons les moins conducteurs (5 × 10-12 Ω-1 cm-1), on a trouvé une énergie d'activation maximum d'environ 1,6 eV.

PACS
7220J - Charge carriers: generation, recombination, lifetime, and trapping.
7361N - Insulators.
7722C - Permittivity (dielectric function).
7722G - Dielectric loss and relaxation.

Key words
carrier density -- carrier mobility -- dielectric losses -- electronic conduction in insulating thin films -- permittivity -- polymer films