Influence de la nature des électrodes sur les propriétés électriques du ZnS en couches minces)

Abstract
The resistivity of ZnS thin films evaporated in high vacuum is studied as a function of temperature. With Al electrodes the resistivity is greater in transverse than longitudinal direction. The current versus potential curves with Au or Al electrodes are not linear, in the transverse direction, but they are linear in the longitudinal direction. The author thinks that there could exist a dissymmetry in the transverse structure of the layers, due to the partial dissociation of ZnS during the evaporation. The current vs potential curves are studied with In electrodes which form a better ohmic contact that Au and Al. The current flowing through the layer increases then more rapidly than the potential. The influence of light and temperature has also been studied.

Résumé
L'auteur étudie, tout d'abord, la résistivité du sulfure de zinc, en couches minces déposées sous vide, en fonction de la température. Avec des électrodes en aluminium la résistivité est plus élevée dans le sens transversal que dans le sens longitudinal. Les caractéristiques courant-tension mesurées dans le sens transversal avec des électrodes en or ou en aluminium ne sont pas linéaires. Dans le sens longitudinal, les caractéristiques sont linéaires. Il semble donc exister une dissymétrie dans la structure transversale des couches, provenant d'une dissociation partielle du ZnS au cours de l'évaporation. On utilise ensuite l'indium comme électrodes et l'on étudie les caractéristiques courant-tension dans le sens longitudinal. L'indium forme un meilleur contact ohmique que l'or et l'aluminium et laisse passer des courants qui augmentent beaucoup plus rapidement que la tension. L'influence de la lumière et de la température sur ces caractéristiques a été étudiée.