Structure magnétique du manganite de fer par diffraction neutronique

Abstract
Mn2FeO4 is a tetragonally distorted spinel belonging to the space group D194h - I41/amd with a cla ratio of about 1.06 (referred to a face centred unit cell). The two oxygen parameters y = 0.025, z = 0.259 and the degree of inversion Δ = 0.1 were determined on the basis of room temperature neutron diffraction powder patterns, at higher angles. Neutron diffraction patterns obtained at 300 °K as well as at 4.2 °K can be indexed in the chemical cell. In the absence of any evidence for a superstructure the magnetic intensities were calculated on the basis of Néel's scheme with ferrimagnetic ordering of SA and SB spins in the basal plane. The value of 0.3 μ B and 2.7 μB have been deduced for the resultant moments at 300 °K and 4.2 °K respectively.

Résumé
Mn2FeO4 est un spinelle à déformation quadratique appartenant au groupe d'espace D194h - I41/amd avec un rapport c/a égal à 1,06 rapporté à une maille à faces centrées. Les deux paramètres de l'oxgène y = 0,025, z = 0,259 et le degré d'inversion Δ = 0,1 ont été déterminés à partir des valeurs des réflexions d'indice élevés du diagramme de neutrons fait à la température ambiante. Toutes les raies des diagrammes de neutrons réalisés à 300 °K et 4,2° s'indexent dans la maille chimique. En l'absence de raies de surstructure les intensités magnétiques ont été calculées suivant un modèle de Néel avec un arrangement ferrimagnétique des spins SA et SB dans le plan de base. Les valeurs de 0,3 μ B et 2,7 μB ont été déduites pour les moments résultants à 300 °K et 4,2 °K.