Copper-deficiency in Ln2-xCexCuO4 (Ln=Nd, Gd) crystals and oxygen disorder in Gd2CuO4 crystals

Abstract
The structure of seven Nd2-xCexCuO4 (x=0 and x=0.18) and Gd2CuO4 single crystals is determined by means of X-ray diffraction. All crystals have the Nd2CuO 4 tetragonal T' structure, space group I4/mmm (139). The copper site is found deficient (3 - 6%) in six crystals whereas both oxygen sites (within the CO2 planes O(1) and between rare earth layers 0(2)) remain fully occupied within standard deviation. The vibration ellipsoids of Nd, Cu and O(2) appear to be more ellongated in the c direction in Nd-based crystals reannealed in an inert atmosphere than in as-grown ones. The oxygen of the CuO2 basal plane (0(1)) in Gd2CuO4 is found off-centered in the a direction by 0.18 (2) Å.

Résumé
La structure de sept monocristaux de Nd2-xCexCuO 4 (x=0 et x=0.18) et Gd2CuO4 est déterminée par diffraction des rayons X. Tous les cristaux ont la structure tétragonale T' du Nd2CuO4 (groupe d'espace I4/mmm, n° 139). Un défaut de cuivre de l'ordre de 3 à 6% est trouvé dans six cristaux alors que les deux sites de l'oxygène (dans les plans CuO2 O(1) et entre les plans de terre rare O(2)) sont complètement occupés dans la limite d'erreur. Les ellipsoïdes de vibration des sites Nd, Cu et O(2) sont plus allongés parallèlement à l'axe c dans les cristaux recuit sous atmosphère inerte que dans les cristaux bruts de croissance. L'atome d'oxygène des plans CuO 2 (O(1)) dans Gd2CuO4 est trouvé décentré dans la direction de l'axe a de 0.18 (2) Å.