J. Phys. France 49, 383-387 (1988)
DOI: 10.1051/jphys:01988004903038300

Systematic copper deficiency in Y-Ba-Cu-O single crystals

G. Collin, A.C. Audier et R. Comes

Laboratoire de Physique des Solides, U.A. 02 C.N.R.S., Bât. 510, Université Paris-Sud, 91405 Orsay, France

Abstract
The structure of five YBa2Cu3-xO7-δ(0.09 ≤δ < 1) crystals is determined by X-Ray diffraction. Four crystals are orthorhombic (δ < 0.35) and twinned with a twin ratio deduced from refinement corresponding to 54-70% of the main sample. The last one is tetragonal (δ = 1). A new feature, not systematically reported, is a deficiency on the Cu(1) site, in the range of 4-8% , whereas the other cationic sites remain fully occupied. The oxygen ordering increases with concentration. The Ba site is found strongly anharmonic.

Résumé
La structure de cinq cristaux de YBa2Cu3-xO 7-6 (0,09) ≤ 1) a été déterminée par diffraction des rayons X. Quatre cristaux sont orthorhombiques (δ < 0,35) et maclés avec un taux de maclage déduit de l'affinement correspondant à 54-70% de l'individu principal. Le dernier est quadratique (δ =1). Un défaut systématique est trouvé sur le site Cu(1), de l'ordre de 4-8% , alors que les autres sites cationiques sont complètement occupés. L'ordre sur l'oxygène croît avec la concentration. Le site Ba est trouvé fortement anharmonique.

PACS
6166F - Inorganic compounds.
7470 - Superconducting materials.

Key words
barium compounds -- crystal atomic structure of inorganic compounds -- type II superconductors -- X ray diffraction examination of materials -- yttrium compounds