J. Phys. France 48, 1407-1412 (1987)
DOI: 10.1051/jphys:019870048090140700

Structure of Ba2 YCu3O6.26 at 20 and 298K by single-crystal neutron diffration

A. Renault¹, G.J. McIntyre², G. Collin³, J.-P. Pouget¹ et R. Comes<sup>1

1</sup>  Laboratoire de Physique des Solides (LA02), Bâtiment 510, Université de Paris-Sud, 91405 Orsay, France
²  Institut Laue-Langevin, 156X, 38042 Grenoble Cedex, France
³  UA200, Université René Descartes, 4 Avenue de l'Observatoire, 75006 Paris, France

Abstract
The crystal structure of Ba2YCu3O8-δ (δ=1.74) at 20K and 298K has been determined by single-crystal neutron diffraction. In contrast to the superconducting orthorhombic phase for which 6 ~ 1.1, this phase crystallizes in the tetragonal space group P4/MMM wtih α = 3.8573(4)Å and c = 11.7913(10)Å. The increase in oxygen vacancies compared to Ba2YCu3O8-δ (6 ˜1.1.) is confined entirely to the sites in the plane midway between pairs of closest barium atoms. No significant differences were observed between the structures at 20K and 298K.

Résumé
La structure cristalline de Ba2YCu3O8-δ (6=1,74) a été déterminée par diffraction des neutrons sur monocristal à 20 K et 298 K. Par opposition à la phase orthorhombique supraconductrice pour laquelle 6 ˜1,1, ce composé cristallise dans le groupe d'espace tétragonal P4/m m m avec α = 3,8573(4)Å et c = 11,7913(10)Å. L'augmentation du nombre de lacunes d'oxygène, par rapport à Ba2YCu3O 8-δ (δ ˜1,1), est entièrement située dans le plan médiateur des pairs d'atomes de barium les plus proches. Aucune différence notable n'a été observée entre les structures à 20 K et 298 K.