J. Phys. France 48, 1981-1989 (1987)
DOI: 10.1051/jphys:0198700480110198100

Partial pair distribution functions in icosahedral Al-Mn studied by contrast variation in neutron diffraction

J.-M. Dubois1 et Ch. Janot2

1  Unité de Sciences et Génie des Matériaux Métalliques, Ecole des Mines, parc de Saurupt, 54042 Nancy, France
2  Institut Laue-Langevin, 156X, 38042 Grenoble, France


Abstract
Icosahedral Al-Mn and Al-(MnFeCr) alloys were studied by neutron diffraction with scattering vectors up to 16 Å-1. The three partial pair distribution functions (PPDF) were obtained and the actual isomorphous substitution of the σ-FeCr mixture for Mn was confirmed. The PPDF for Mn-Mn indicates the existence of a manganese subnetwork rather similar to that found in the α(AlMnSi) crystalline phase. In particular the shortest Mn-Mn distances were found at 4.47 and 4.97 A.


Résumé
Des phases icosaédriques des systèmes Al-Mn et Al-(MnFeCr) ont été étudiées par diffraction des neutrons, jusqu'à des vecteurs de diffusion de 16 Å -1. Les trois fonctions de distribution de paires partielles ont été calculées. On a pu ainsi confirmer sans ambiguïté le caractère parfaitement isomorphe de la substitution du Mn par σ-FeCr. Les corrélations de paires atomiques apparaissent très semblables à celles de la phase cristalline α(AlMnSi). En particulier, les plus courtes distances Mn-Mn sont trouvées à 4,47 et 4,97 A.

PACS
6166D - Alloys.

Key words
aluminium alloys -- chromium alloys -- crystal atomic structure of alloys -- iron alloys -- manganese alloys -- neutron diffraction examination of materials -- quasicrystals