| Numéro |
J. Phys. France
Volume 50, Numéro 8, avril 1989
|
|
|---|---|---|
| Page(s) | 923 - 935 | |
| DOI | https://doi.org/10.1051/jphys:01989005008092300 | |
J. Phys. France 50, 923-935 (1989)
DOI: 10.1051/jphys:01989005008092300
1 Groupe de Physique des Solides de l'ENS, Université Paris V, Tour 23, 2 place Jussieu, 75251 Paris Cedex 05, France
2 I.F.F., K.F.A., D-5170 Jülich, F.R.G.
6220M - Fatigue, brittleness, fracture, and cracks.
4650 - Fracture mechanics, fatigue and cracks.
6141 - Polymers, elastomers, and plastics.
6860 - Physical properties of thin films, nonelectronic.
Key words
cracks -- polymer films
DOI: 10.1051/jphys:01989005008092300
Formation of periodic crack structures in polydiacetylene single crystal thin films
J. Berréhar1, C. Lapersonne-Meyer1, M. Schott1 et J. Villain21 Groupe de Physique des Solides de l'ENS, Université Paris V, Tour 23, 2 place Jussieu, 75251 Paris Cedex 05, France
2 I.F.F., K.F.A., D-5170 Jülich, F.R.G.
Abstract
The formation of a regular pattern of periodic cracked ridges on single crystal polydiacetylene films is described. Films thicker than a certain critical thickness are cracked while thinner ones are not. A model in the framework of linear elasticity theory is developed, which accounts for this transition as a function of the film thickness.
Résumé
Nous décrivons ici les conditions d'apparition d'un réseau de fractures périodiques dans des films monocristallins de polydiacétylène. Les films dont l'épaisseur est supérieure à une certaine épaisseur critique présentent ces fractures, tandis que les plus minces ne sont pas fracturés. Un modèle basé sur la théorie élastique linéaire rend compte de cette épaisseur critique.
6220M - Fatigue, brittleness, fracture, and cracks.
4650 - Fracture mechanics, fatigue and cracks.
6141 - Polymers, elastomers, and plastics.
6860 - Physical properties of thin films, nonelectronic.
Key words
cracks -- polymer films