J. Phys. France 47, 1233-1238 (1986)
DOI: 10.1051/jphys:019860047070123300

Back to the A15 instability problems

A.F. Khoder¹, J. Labbé², M. Couach¹ et J.P. Sénateur<sup>3

1</sup>  Service des Basses Températures, CEN Grenoble, 85 X, 38041 Grenoble Cedex, France
²  Ecole Normale Supérieure, GPS, 24, rue Lhomond, 75231 Paris Cedex 05, France
³  ENSIEG-ER 155, B.P. 46, 38042 St-Martin-d'Hères, France

Abstract
Recent experimental results obtained on A15 compounds allow a better understanding of the correlation between superconductivity and lattice instability in this system. The effect of the lattice distortion is shown to reduce the superconducting transition T c. An enhancement of Tc in the case of V3Si is obtained when the temperature of the martensitic transition is lowered (by pressure or defects). Theoretically, these effects are well explained and predictable within the frame work of the band Jahn-Teller « models »; then also give more arguments in favour of these models.

Résumé
De récents résultats expérimentaux sur les composés A15 permettent une meilleure compréhension de la relation entre la supraconductivité et l'instabilité de réseau dans ce système. L'effet de la déformation structurale est de réduire la température de transition supraconductrice Tc. Une augmentation de Tc, dans le cas de V 3 Si, est obtenue lorsque la température de la transition structurale est abaissée (par effet de pression ou de défauts). 11 est possible, d'un point de vue théorique, de comprendre et de prévoir ces effets dans le cadre des modèles Jahn-Teller de bandes, ce qui donne des arguments supplémentaires en faveur de ce mécanisme.

PACS
7410 - Occurrence, potential candidates.
7470 - Superconducting materials.

Key words
Jahn Teller effect -- martensitic transformations -- superconducting transition temperature -- type II superconductors