An electrochemically reduced graphite-cobalt compound : synthesis and magnetic study

R. Yazami¹, G. Chouteau², Ph. Touzain¹ et A. Briggs<sup>2

1</sup>  Laboratoire d'Adsorption et Réaction du Gaz sur Solides, Ecole Nationale Supérieure d'Electrochimie et d'Electrométallurgie de Grenoble, BP 75, 38402 Saint-Martin-d'Hères Cedex, France
²  Service National des Champs Intenses/Centre de Recherches sur les Très Basses Températures, Centre National de la Recherche Scientifique, 25 avenue des Martyrs, BP 166 X, 38042 Grenoble Cedex, France

Abstract
When it is used as a cathode material in a lithium primary battery, graphite intercalation compound with CoCl2 is electrochemically reduced during the discharge process. This reaction leads to the formation of a new Co-graphite compound which is characterized by chemical and X-ray analysis. The magnetic properties exhibit a spin-glass behaviour at low temperature, due to the islandic character of the compound. Similarities with the 2-dimensional CoCl2 compound are also found.

Résumé
Quand on l'utilise comme cathode dans une pile au lithium, le composé intercalaire du graphite CoCl2 est réduit pendant la décharge. Cette réaction conduit à la formation d'un nouveau composé du cobalt qu'on a caractérisé par une analyse chimique et aux rayons X. Aux basses températures, ses propriétés magnétiques sont celles d'un verre de spin. La comparaison avec le composé intercalaire à deux dimensions CoCl2 montre beaucoup de similitudes.