J. Phys. France 38, 1449-1455 (1977)
DOI: 10.1051/jphys:0197700380110144900

Synthesis, magnetic properties and 57Fe Mössbauer study of the laves phase compound YbFe2

C. Meyer¹, B. Srour¹, Y. Gros¹, F. Hartmann-Boutron¹ et J.J. Capponi<sup>2

1</sup>  Laboratoire de Spectrométrie Physique , B.P. 53, 38041 Grenoble Cedex, France
²  Laboratoire de Cristallographie du C.N.R.S. , B.P. 166 X, 38042 Grenoble Cedex, France

Abstract
The cubic MgCu2-type compound YbFe2 was synthesised at 1 200 °C under 80 kbar pressure and characterized by means of X-ray diffraction. The temperature dependent magnetization exhibits a compensation point at 31 K. The Môssbauer spectra shows that at very low temperature the magnetization is parallel to a < 100 > direction. As the temperature increases the magnetization probably slightly deviates from this direction.

Résumé
Le composé cubique YbFe2, de structure MgCu2, a été synthétisé à 1 200°C sous 80 kbar et identifié par diffraction des rayons X. La courbe d'aimantation en fonction de la température présente un point de compensation à T = 31 K. Les spectres Mössbauer indiquent qu'à très basse température l'aimantation est parallèle à une direction < 100 >. Quand la température s'élève, l'aimantation semble légèrement s'écarter de cette direction.

PACS
7550G - Ferrimagnetics.
7560E - Magnetization curves, hysteresis, Barkhausen and related effects.
7680 - Mössbauer effect; other gamma-ray spectroscopy.

Key words
ferrimagnetic properties of substances -- iron alloys -- magnetisation -- Mossbauer effect -- ytterbium alloys