Propriétés diélectriques de l'oxyde cuivreux aux audiofréquences entre 150 °K et 320 °K

Abstract
The dielectric properties of poly and monocristalline Cu2O samples were investigated as a function of frequency from 40 Hz to 100 kHz. At 273 °K, the dielectric constant and the dielectric loss of all samples show similar dispersion with caracteristic frequencies between 100 Hz and 300 Hz. The dispersion intensity is related to the static conductivity. Below 150 °K no dispersion is observed. The thermal analysis (150 °K - 320 °K) shows that two components contribute essentially to the spectra. A third low intensity component is observed with some samples. The variation of the static bulk resistivity is exponential in that temperature range.

Résumé
Les propriétés diélectriques d'échantillons de Cu2O poly et monocristallins ont été étudiées entre 40 Hz et 100 kHz. A 273 °K, la constante et les pertes diélectriques de tous les échantillons présentent des dispersions semblables dont les fréquences caractéristiques se situent entre 100 Hz et 300 Hz. L'intensité de cette dispersion est liée à la conductibilité statique. En dessous de 150 °K environ, aucune dispersion ne se manifeste. L'analyse thermique (150 °K - 320 °K) du phénomène montre que le spectre est essentiellement formé par la contribution de deux composantes. Une troisième composante de moindre intensité est parfois observée. Dans le domaine de températures étudié, la variation de la résistance statique de volume est toujours exponentielle.