J. Phys. France 26, 317-320 (1965)
DOI: 10.1051/jphys:01965002606031700

Contribution à l'étude de la constante diélectrique de la cuprite. I. Détermination de la constante diélectrique par des méthodes optiques

Claude Noguet^{1, 2}, Claude Schwab^{1, 2}, Christopher Sennett^{1, 2}, Manuel Sieskind^{1, 2} et Claude Viel<sup>1, 2

1</sup>  Laboratoire de Spectroscopie et d'Optique du Corps Solide, Institut de Physique
²  Laboratoire de Chimie Organique des Substances Naturelles, Institut de Chimie, Université de Strasbourg

Abstract
The dielectric constant of cuprous oxide has been measured by an optical method for frequencies varying from 50 cm-1 to 4 000 cm -1. The extrapolated value of ε is found to be ε stat = 7.5 ± 0:2. The dispersion curve may be represented by a formula of the type [FORMULA] in terms of the two infra-red active frequencies ν 1 and ν2. From this it is possible to deduce the effective charge on the ions, which is 0.34 and - 0.68 électron charge for the copper and oxygen ions respectively. This corresponds to a weakly ionic crystal.

Résumé
La constante diélectrique ε de Cu2O a été mesurée par une méthode optique et pour des nombres d'onde variant de 4 000 à 50 cm -1. La valeur de ε extrapolée donne : εstat = 7,5 ± 0,2. La courbe de dispersion peut-être représentée par une formule du type [FORMULE]faisant intervenir les deux fréquences actives dans l'infrarouge ν1 et ν 2. On en déduit que la charge effective portée par les ions est de 0,34 électron pour le cuivre, et - 0,68 électron pour l'oxygène, ce qui correspond à une faible ionicité de la cuprite.

PACS
77 - Dielectrics, piezoelectrics, and ferroelectrics and their properties.

Key words
copper compounds -- dielectric properties -- optical constants