J. Phys. France 24, 522-524 (1963)
DOI: 10.1051/jphys:01963002407052200

Étude du recuit des défauts, par mesure de l'anisotropie magnétique d'un alliage de fer-nickel, après irradiation

Jean Paulevé et Daniel Dautreppe

Section de Physique du Solide. C. E. N. de Grenoble

Abstract
A uniaxial magnetic anisotropy is induced by neutron bombardment with an applied magnetic field in Fe-Ni (50%-50%) samples. This anisotropy is caused by a new orderdisorder transition. After an irradiation at 30°C, the annealing kinetics of the defects is studied by means of the magnetic anisotropy increase. In most cases the law ΔE = a Log (bt + 1) is verified very well. This law can be explained by a second order reaction for the annealing of the defects. After an irradiation at 78 °K an isochronal annealing indicates that the defects which give rise to an enhancement of the diffusion process, begin to move only at 100 °K. The interstitials do not seem to contribute to the ordering process.

Résumé
Une anisotropie magnétique uniaxiale est créée par bombardement sous champ magnétique d'échantillons de Fe-Ni (50 %-50 %). Cette anisotropie est due à une nouvelle transition ordre-désordre. Après irradiation à 30°C, la cinétique de recuit des défauts est étudiée en suivant l'accroissement d'anisotropie. Dans la plupart des cas une loi ΔE = a Log ( bt + 1) est très bien vérifiée. On explique cette loi par une cinétique de recuit du deuxième ordre. Après une irradiation à 78 °K un recuit isochrone indique que les défauts accélérant la diffusion ne se manifestent qu'à partir de 100 °K. Les interstitiels ne semblent pas contribuer à la mise en ordre.

PACS
6180H - Neutron radiation effects.
6172 - Defects and impurities in crystals; microstructure.
8140G - Other heat and thermomechanical treatments.
7550 - Studies of specific magnetic materials.

Key words
crystal defects -- heat treatment -- iron compounds -- ferromagnetic materials -- neutron effects -- phase transformations