Orthorhombicity and oxygen uptake by YBa2Cu3O6 + x
Michel Ain1, Jean-Marc Delrieu1, Alain Menelle2, George Parette2 et Jocelyne Jegoudez31 Service de Physique du Solide et de Résonance Magnétique, Direction de la Physique, CEN-Saclay, 91191 Gif-sur-Yvette Cedex, France
2 Laboratoire Léon Brillouin (CEA-CNRS) CEN-Saclay, 91191 Gif-sur-Yvette Cedex, France
3 Chimie des Solides, Université de Paris-Sud, 91405 Orsay, France
Abstract
We have measured, at different oxygen contents, the cell parameters of YBa2Cu3O6+x between 24 and 260 K using cold neutrons. The results of profile refinement of our high resolution data is shown in figure 1 ; it does not confirm the X-ray finding, recently reported [1], showing a cusp in the orthorhombic splitting b - a, around the superconducting transition temperature. It has also been evidenced that the volume of the crystallographic cell is contracted by oxygen uptake.
Résumé
Nous avons mesuré, à différents taux d'oxygène, les paramètres de maille de YBa2Cu3O6+x entre 24 et 260 K à l'aide de neutrons froids. L'affinement de nos résultats, présenté sur la figure 1, ne nous permet pas de confirmer les mesures de rayons-X, récemment publiées [1], montrant une anomalie de l'orthorhombicite b - a, au voisinage de la température de transition supraconductrice. Il a aussi, été mis en évidence que le volume de la maille cristallographique se contractait par absorption d'oxygène.